Corrosione atmosferica in area urbana-costiera di un acciaio Cor-Ten: studio del rilascio in ambiente dei metalli di lega

Cor-Ten is a particular kind of steel, belonging to low-alloyed steel; thanks to his aesthetic features and resistance to atmospheric corrosion, this material is largely used in architectural, artistic and infrastructural applications. After environmental exposure, Cor-Ten steel exhibits the characteristic ability to self-protect from corrosion, by the development of a stable and adherent protective layer. However, some environmental factors can influence the formation and stability of the patina. In particular, exposure of Cor-Ten to polluted atmosphere (NOx, SOx, O3) or coastal areas (marine spray) may cause problems to the protective layer and, as a consequence, a release of alloying metals, which can accumulate near the structures. Some of these metals, such as Cr and Ni, could be very dangerous for soils and water because of their large toxicity. The aim of this work was to study the corrosion behavior of Cor-Ten exposed to an urban-coastal site (Rimini, Italy). Three different kinds of commercial surface finish (bare and pre-patinated, with or without a beeswax covering) were examined, both in sheltered and unsheltered exposure conditions. Wet deposition brushing the specimens surface (leaching solutions) are monthly collected and analyzed to evaluate the extent of metal release and the form in which they leave the surface, for example, as water-soluble compounds or non-adherent corrosion products. Five alloying metals (Fe, Cu, Cr, Mn and Ni) and nine ions (Cl-, NO3-, NO2-, SO42-, Na+, Ca2+, K+, Mg2+, NH4+) are determined through Atomic Absorption Spectroscopy and Ion Chromatography, respectively. Furthermore, the evolution and the behaviour of the patina are periodically followed by surface investigations (SEM-EDS and Raman Spectroscopy). After two years of exposure, the results show that Bare Cor-Ten, cheaper than the other analyzed specimens, even though undergoes the greater mass variation, his metal release is comparable to the release of the pre-patinated samples. The behavior of pre-patinated steel, with or without beeswax covering, do not show particular difference. This exposure environment doesn’t allow a completely stabilization of the patina; nevertheless an estimate of metal release after 10 years of exposure points out that the environmental impact of Cor-Ten is very low: for example, the release of chromium in the soluble fraction is less than 10 mg if we consider an exposed wall of 10 m2.