On the characterization of the mechanical behaviour of bonded steel-CFRP adhesive joints

The use of adhesively bonded carbon fiber reinforced polymers (CFRP) is well established to repair metallic structural elements in the aerospace industry for more than three decades. Despite a few exceptions, this technology has yet not been exploited for the steel construction industry where there is a great need to rehabilitate old metallic bridges. For instance, in Europe more than 30% of the railway bridge stock operated for more than 100 years. These bridges are made of old mild steel or puddle iron that exhibits poor behaviour due to the quality of the material itself and degradation caused by the long-term loading or environmental effects. The modest results for Steel/CFRP joints obtained may be due to the type of adhesive used. In fact, most of the previous studies utilized brittle adhesives specially developed for concrete structures. Recent ductile adhesives that made for the automotive industry for metallic joints should be more appropriate. In this study, an experimental investigation on the behaviour of CFRP/steel adhesively bonded joints is presented. A comparison between brittle adhesives and ductile adhesives is conducted. The results show that the ductile adhesives achieve much higher performance than the brittle ones. The brittle adhesives provide more stiffness to the adhesive joint. In the specimens with the ductile adhesives, the failure pattern started by yielding the steel bars first then the adhesive joint which is promising since it can facilitate the design significantly if the steel yielding can be used as a design criterion. The main disadvantage of ductile adhesives is they are usually more expensive than brittle ones. In order to solve this issue, bi-adhesive joints, in which the joint is mainly made of (low cost) brittle adhesive and ductile adhesive in the stress concentration region, are proposed. The results revealed very high improvement up to the yielding strength of the steel bars and with a balanced stiffness.